PENGARUH MEDIA PENDINGIN DALAM

PROSES PWHT PENGELASAN SMAW

PADA MATERIAL BAJA ASTM A36

TERHADAP KEKUATAN TARIK

DAN STRUKTUR MIKRO

THE EFFECT OF COOLING MEDIA IN THE SMAW WELDING PWHT PROCESS ON ASTM A36 STEEL MATERIAL ON TENSILE STRENGTH AND MICRO STRUCTURE

Penelitian ini bertujuan untuk mengetahui pengaruh

variasi media pendingin dalam proses Post Weld Heat Treatment

(PWHT) terhadap kekuatan tarik dan struktur mikro hasil

pengelasan Shielded Metal Arc Welding (SMAW) pada baja ASTM

A36. Proses PWHT dilakukan pada suhu 780°C dengan waktu

tahan selama 60 menit, diikuti oleh pendinginan menggunakan

media udara, pasir, tungku, dan tanpa media pendingin.

Penelitian menggunakan metode eksperimen di

laboratorium Jurusan Teknik Mesin Politeknik Negeri Malang,

dengan pengujian meliputi uji tarik dan struktur mikro. Hasil uji

tarik menunjukkan bahwa media pendingin udara memberikan

nilai kekuatan tarik tertinggi sebesar 268,8 MPa, sedangkan

pendingin tungku menghasilkan nilai terendah sebesar 247,16

MPa. Pendinginan udara menghasilkan laju pendinginan tercepat

yang berdampak pada peningkatan kekuatan tarik, sedangkan

pendinginan lambat seperti pada tungku cenderung menurunkan

kekuatan tarik. Struktur mikro yang terbentuk mencakup fasa

ferrit, perlit, dan martensit, dengan dominasi yang bervariasi

tergantung pada media pendingin yang digunakan. Pendinginan

udara dan tanpa media pendingin menunjukkan distribusi ferrit

dan perlit yang seimbang, sementara pendinginan pasir dan

tungku menunjukkan kecenderungan peningkatan ferrit dan perlit

berukuran lebih besar, yang meningkatkan keuletan tetapi

menurunkan kekuatan tarik.

Hasil analisis statistik menggunakan uji T menunjukkan

adanya perbedaan signifikan antara variasi media pendingin

terhadap kekuatan tarik. Dengan demikian, media pendingin

This research aims to investigate the effect of different cooling

media in the Post Weld Heat Treatment (PWHT) process on the

tensile strength and microstructure of ASTM A36 steel welded using

Shielded Metal Arc Welding (SMAW). The PWHT process was

conducted at a temperature of 780°C with a holding time of 60

minutes, followed by cooling using air, sand, furnace, and no specific

cooling medium.

The experimental method was carried out in the Mechanical

Engineering Laboratory of the State Polytechnic of Malang, with

tensile and microstructural testing performed on the specimens.

Tensile test results showed that air cooling produced the highest

tensile strength at 268.8 MPa, while furnace cooling resulted in the

lowest at 247.16 MPa. Faster cooling rates, as in air cooling, improved

tensile strength, while slower cooling rates, such as furnace cooling,

tended to reduce it. The resulting microstructures included ferrite,

pearlite, and martensite phases, with the dominance of each phase

varying depending on the cooling media. Air and non-media cooling

exhibited a balanced distribution of ferrite and pearlite, while sand and

furnace cooling resulted in coarser grains, increasing ductility but

reducing tensile strength.

Statistical analysis using the independent sample t-test

showed significant differences between the cooling media variations in

terms of tensile strength. Therefore, the choice of cooling media plays

a crucial role in determining the mechanical properties of welds and