PENGARUH FAKTOR AIR SEMEN TERHADAP PENGGUNAAN

LIMBAH TIANG PANCANG SEBAGAI AGREGAT KASAR

PADA PEMBUATAN BETON MUTU NORMAL

THE EFFECT OF CEMENT WATER FACTORS ON THE USE 

OF POLE WASTE AS A RUDE AGGREGATE 

IN THE MAKING OF NORMAL QUALITY CONCRETE

Menurut Febriyatno dalam jurnal Hanafiah tahun 2003, Beton normal adalah beton yang mempunyai kuat tekan berkisar antara 200–500 kg/cm2, beton ini mempunyai porsi terbesar produksi beton di Indonesia dan sering dijumpai misalkan, di pabrik beton precast dan balok-balok beton pratekan, serta pembuatan gedung bertingkat. Di Indnesia, skala pembangunan semakin meningkat sehingga berakibat pada meningkatnya kebutuhan material akan konstruksi seperti air, agregat halus dan agregat kasar. Alam merupakan penghasil terbesar agregat dan apabila dipergunakan secara terus-menerus maka lama-kelamaan persediaan menjadi berkurang. Salah satu alternatif pemecahannya yaitu dengan memakai limbah beton.

Tujuan penelitian ini berdasarkan rumusan masalah di atas yaitu untuk mengetahui pengaruh Variasi Faktor Air Semen (FAS) terhadap penggunaan limbah tiang pancang sebagai agregat kasar pada pembuatan beton mutu normal.

Hasil penelitian menujukan bahwa diantara variasi fas 0.24, 0.26, 0.28, 0.30, dan 0.32 didapat kuat tekan beton terbesar pada variasi fas 0.32 dengan hasil kuat tekan sebesar 24,16 MPa pada hari ke-28. Sedangkan kuat tekan terendah berada pada variasi fas 0.24 yaitu sebesar 15.49 MPa di hari ke 7. Dari hasil yang diperoleh, dapat disimpulkan bahwa semakin besar faktor air semen, maka kuat tekan pada beton akan semakin kuat dan semakin kecil faktor air semen, maka kuat tekan pada beton semakin berkurang.

Kata kunci: beton normal, limbah tiang pancang, superplasticizer, variasi fas, kuat tekan

According to Febriyatno in the Hanafiah journal in 2003, normal concrete is concrete that has a compressive strength ranging from 200-500 kg / cm2, this concrete has the largest portion of concrete production in Indonesia and is often found, for example, in precast concrete factories and prestressed concrete blocks, and construction of multi-storey buildings. In Indonesia, the scale of development is increasing, resulting in an increase in the need for construction materials such as water, fine aggregate and coarse aggregate. Nature is the largest producer of aggregates and if it is used continuously, the supply will decrease over time. One alternative solution is to use concrete waste.

The purpose of this research is based on the problem formulation above, namely to determine the effect of Cement Water Factor Variation (FAS) on the use of pile waste as coarse aggregate in the manufacture of normal quality concrete.

The results showed that among the variations of the fas 0.24, 0.26, 0.28, 0.30, and 0.32, the greatest compressive strength of concrete was found in the 0.32 fas variation with a compressive strength of 24.16 MPa on the 28th day. While the lowest compressive strength is in the fas variation of 0.24, which is 15.49 MPa on day 7. From the results obtained, it can be concluded that the greater the cement water factor, the stronger the compressive strength of the concrete and the smaller the cement water factor, the compressive strength. on concrete is decreasing.

Keywords: normal concrete, pile waste, superplastizicer, variation of facies, compressive strength.