PENGARUH KOMPOSISI LARUTAN CETAK POLIMER ELEKTROLIT Polyvinylidene fluoride (PVDF) TERHADAP KINERJA DYE SENSITIZED SOLAR CELL (DSSC) BERBASIS NATURAL PHOTOSENSITIZER BUNGA TELANG (Clitoria ternatea)

EFFECT OF THE COMPOSITION OF POLYMER ELECTROLITE Polyvinylidene fluoride (PVDF) COATING  SOLUTION ON THE PERFORMANCE OF DYE SENSITIZED SOLAR CELL (DSSC) BASED ON NATURAL PHOTOSENSITIZER OF TELANG FLOWER (Clitoria ternatea)

Dye Sensitized Solar Cell (DSSC) merupakan teknologi yang menjanjikan dalam konversi energi matahari ke energi listrik. Namun, dalam pengembangannya, ditemukan permasalahan terkait kebocoran maupun penguapan elektrolit cair. Kondisi dapat menurunkan stabilitas DSSC. Sistem DSSC terdiri dari fotoanoda, elektrolit, elektroda pembanding dan pewarna (dye) dengan prinsip kerja fotoelektrokimia. Dalam mengatasi permasalahan tersebut, polimer dari Polyvinylidene fluoride (PVDF) menjadi solusi dari permasalahan dengan cara meningkatkan mobilitas ion I- /I₃^- pada elektrolit. memiliki nilai konduktivitas ionik dan kinerja jangka panjang. Komposisi polimer berpengaruh pada konduktivitas ionik yang berdampak pada aliran elektron sistem DSSC. Oleh karena itu, pada penelitian ini dilakukan optimasi komposisi pembuatan elektrolit polimer PVDF/DMAc (%) yaitu 12/88/, 14/86, 16/84, 18/82, dan 20/80. Photosensitiser dalam penelitian ini menggunakan ekstrak bunga telang yang dikarakterisasi menggunakan instrumen Spektrofotometer UV-Vis untuk mengetahui serapan panjang gelombang dan didapatkan panjang gelombang spesifik pada 573 nm, yang menandakan pewarna tersebut berada dalam daerah visible. Karakterisasi elektrokimia dari pewarna menggunakan voltametri, dihasilkan energi celah pita dihasilkan nilai bandgap 0,5114 eV. Kinerja dan stabilitas DSSC dilakukan dievaluasi dengan pengukuran tegangan dan arus menggunakan multimeter serta ddilakukan perhitungan fill factor dan efisiensi. Diperoleh kinerja DSSC dengan dengan elektrolit cair sebesar 1,662%, sedangkan DSSC dengan elektrolit membran komposisi terbaik (18/82) sebesar 1,4052 %. pada waktu 0 jam. Selain itu dilakukan uji kinerja pada waktu pendiaman 72 jam, dihasilkan efisiensi sebesar 1,170% sedangkan DSSC dengan elektrolit membran komposisi terbaik (18/82) sebesar 1,336%. Hal tersebut menunjukkan penurunan efisiensi DSSC dengan elektrolit cair sebesar 29,605 % sedangkan DSSC elektrolit membran sebesar 4 – 12 %.

Kata Kunci: : DSSC, Elektrolit Membran, Polyvinylidene fluoride, Stabilitas

Dye Sensitized Solar Cell (DSSC) is a promising technology in the conversion of solar energy to electrical energy. However, in its development, there are problems related to leakage or evaporation of liquid electrolyte. These conditions can reduce the stability of the DSSC. DSSC system consists of photoanode, electrolyte, comparison electrode and dye with photoelectrochemical working principle. In overcoming these problems, polymers from Polyvinylidene fluoride (PVDF) are the solution to the problem by increasing the mobility of I- /I3- ions in the electrolyte. has ionic conductivity value and long-term performance. The polymer composition affects the ionic conductivity which has an impact on the electron flow of the DSSC system. Therefore, this study optimised the composition of PVDF/DMAc polymer electrolyte (%), namely 12/88/, 14/86, 16/84, 18/82, and 20/80. The photosensitiser in this study uses telang flower extract which is characterised using a UV-Vis Spectrophotometer instrument to determine the wavelength absorption and obtained a specific wavelength at 573 nm, which indicates that the dye is in the visible region. Electrochemical characterisation of the dye using voltammetry, the resulting bandgap energy produced a bandgap value of 0.5114 eV. The performance and stability of the DSSC were evaluated by measuring the voltage and current using a multimeter and calculating the fill factor and efficiency. The performance of DSSC with liquid electrolyte was 1.662%, while DSSC with membrane electrolyte of the best composition (18/82) was 1.4052% at 0 hour. In addition, a performance test was carried out at a 72-hour dwell time, resulting in an efficiency of 1.170% while DSSC with the best composition membrane electrolyte (18/82) was 1.336%. This shows a decrease in the efficiency of DSSC with liquid electrolyte by 29.605%, while the membrane electrolyte DSSC is 4-12%.

Keywords: DSSC, Electrolyte Membrane, Polyvinylidene fluoride, Stability