EFEK PERLAKUAN PANAS ARTIFICIAL AGING

PADA AL₆₀₆₁ TERHADAP TINGKAT KEKERASAN DAN UJI IMPACT

EFFECT OF HEAT TREATMENT WITH ARTIFICIAL AGING

IN AL6061 TO HARDNESS LEVELS AND IMPACT TESTS

ABSTRAK

EFEK PERLAKUAN PANAS ARTIFICIAL AGING

PADA AL6061 TERHADAP TINGKAT KEKERASAN DAN UJI IMPAK

Nama                             :  Danny Arya Wibawa

NIM                                :  16050754067

Program Studi            :  S1 Teknik Mesin

Jurusan                          :  Teknik Mesin

Fakultas                        :  Fakultas Teknik

Nama Lembaga          :  Universitas Negeri Surabaya

Dosen Pembimbing  :  Arya Mahendra Sakti, S.T., M.T.

Banyak sekali industri pengecoran yang menerima permintaan pembuatan komponen propeller dari bahan aluminium, namun propeller dari bahan tersebut kurang optimal dilihat dari sisi ketangguhan material dan seringkali mengalami patah karena benturan batu atau karang,, Tujuan penelitan ini adalah membuat paduan aluminium yang diberi perlakuan proses artificial aging untuk mendapatkan nilai kekerasan dan kekuatan impact.

Penelitian ini menggunakan metode penelitian experimen dengan variasi waktu tahan aging yaitu 4 jam, 5 jam, dan 6 jam. Setelah itu di uji nilai kekerasan dan kekuatan impact.

Harapan hasil penelitian ini adalah untuk mendapatkan nilai kekerasan dan kekuatan impact yang optimal dari proses variasi aging.

Kata Kunci: Artifical aging, holding time, nilai kekerasan, dan kekuatan impact,

ABSTRACT

EFFECT OF HEAT TREATMENT WITH ARTIFICIAL AGING

IN AL6061 TO HARDNESS LEVELS AND IMPACT TESTS

Name                                  :  Danny Arya Wibawa

ID Number                        :  16050754067

Study Program                :  Bachelor of Mechanical Engineering

Consentration                   :  Manufacture

Departement/Faculty       :  Mechanical Engineering/Engineering

Institution                         :  State University of Surabaya

Mentor                               :  Arya Mahendra Sakti, S.T., M.T.

Lots of foundry industries have received requests for the manufacture of propeller components from aluminum, but propellers from these materials are not optimal in terms of material toughness and often break due to rock or coral impacts. The purpose of this research is to make aluminum alloy treated with an artificial aging process. to get hardness and impact strength values.

This study used experimental research methods with variations in aging time, namely 4 hours, 5 hours, and 6 hours. After that, the hardness value and impact strength were tested.

The hope of the results of this study is to obtain optimal hardness and impact strength values from the aging variation process.

Keywords: Artificial aging, holding time, hardness value, and impact strength.