Kuat Tekan Beton Fc’ 30 MPa Dengan Penambahan Admixture Sebesar 0.05%, 0.09%, 0.13% Dari Berat Semen
Concrete Compressive Strength Fc' 30 MPa With The Addition Of Admixture Of 0.05%, 0.09%, 0.13% By Weight Of Cement
Tulisan ini bertujuan untuk mengetahui kuat tekan beton silinder dengan rancang campur mutu fc’ 30MPa dengan tambahan Air Entraining Addmixture untuk mengetahui pengaruh bahan tambah tersebuat terhadap kuat tekan beton. Berdasarkan brosur Air Entraining, bahan tambah ini bersifat polimer yang larut dalam air yang befungsi untuk meningkatkan mengurangi berat beton dan mengurangi pemakaian semen dalam campuran.Uji coba campuran beton dibagi dalam tiga perlakuan/ tiga komposisi yaitu dengan dosis Air Entraining masing-masing 0,05%, 0,09%, dan 0,13% dari berat semen. Komposisi bahan campuran beton di tiap mix design tersusun atas 22,26 kg semen, 48,7 kg agregat halus, 22,08 kg agregat kasar ukuran 5-12 mm, 41,04 kg agregat kasar ukuran 10-20 mm, air 8,50 kg.Hasil uji kuat tekan pada beton silinder dengan bahan tambah Air Entraining sejumlah 0,13% pada umur 28 hari sebesar 26,85 MPa. Kuat tekan beton silinder dengan bahan tambah Air Entraining sejumlah 0,09% pada umur 28 hari sebesar 28,25 MPa. Selanjutnya untuk kuat tekan beton silinder dengan bahan tambah Air Entraining sejumlah 0.05% pada umur 28 hari sebesar 30,3 MPa.
Kata kunci: bahan tambah Air Entraining Addmixture, kuat tekan, Beton.
This paper aims to determine the compressive strength of cylindrical concrete with mixed quality design fc’ 30MPa with additional Air Entraining Admixture to determine the effect of the added material on the compressive strength of concrete. Based on brochure Air Entraining, this additive is in nature polymer which dissolves in water which functions to increase the weight of the concrete and reduce the use of cement in the mixture. The concrete mix trials were divided into three treatments/three compositions, namely with Air Entraining 0.05%, 0.09% and 0.13% respectively by weight of cement. The composition of the concrete mixture in mix design composed of 22.26 kg of cement, 48.7 kg of fine aggregate, 22.08 kg of coarse aggregate of 5-12 mm size, 41.04 kg of coarse aggregate of 10-20 mm size, 8.50 kg of water. The compressive strength test results at cylindrical concrete with additives Air Entraining 0.13% at 28 days of age of 26.85 MPa. Compressive strength of cylindrical concrete with additives Air Entraining 0.09% at 28 days of age of 28.25 MPa. Furthermore, for the compressive strength of cylindrical concrete with added materials Air Entraining 0.05% at 28 days of age of 30.3 MPa.
Keywords: additives, Air Entraining Admixture, compressive strength, Concrete.