PENGARUH FRAKSI VOLUME DAN ARAH SERAT KOMPOSIT HIBRID FIBRE METAL LAMINATE (FML) BERMATRIK POLYESTER 157 BQTN-EX TERHADAP KEKUATAN TARIK DAN BENDING

THE EFFECT OF VOLUME FRACTION AND FIBRE DIRECTION OF FIBRE METAL LAMINATE (FML) HYBRID COMPOSITE WITH POLYESTER 157 BQTN-EX MATRIX ON TENSILE AND BENDING STRENGTH

Perkembangan olah raga dari masa ke masa terus mengalami evolusi dalam berbagai aspek. Dahulu, olah raga hanya mengandalkan kekuatan otot dan pikiran. Tapi, di jaman dimana teknologi sudah menjadi bagian dari kebutuhan hidup seperti sekarang, perangkat olah raga pun akhirnya turut dikembangkan untuk meningkatkan performa para pelaku olah raga. Jumlah atlet yang kian bertambah tentu berdampak pada ketatnya persaingan. Di cabang tenis, salah satu perangkat yang dikembangkan secara serius adalah raket. Untuk mengembangkan inovasi pada material raket tenis, maka perlu adanya inovasi pada bidang material maju, salah satunya adalah komposit hibrid (hybrid composite) yang dilaminasi dengan metode Fibre Metal Laminate (FML). Sifat dan kekuatan mekanis komposit hibrid FML dipengaruhi oleh beberapa faktor salah satunya adalah arah serat dan fraksi volume serat. Untuk mendapatkan kombinasi arah serat dan fraksi volume yang tepat, maka perlu adanya banyak penelitian yang dilakukan.
Penelitian ini menggunakan jenis penelitian eksperimen dengan membuat bahan komposit hibrid FML dengan skin komposit Alumunium Al 6061 dan laminasi berpenguat serat rami dan e-glass yang masing–masing variabel akan diuji bending dan uji tarik. Spesimen yang sudah diuji tarik dan bending kemudian dianalisa pengaruh dari variabel bebas terhadap variabel terikat. Variabel bebas meliputi fraksi volume serat 40% dan 60% serat arah serat 0odan 90o.
Berdasarkan hasil penelitian dapat disimpulkan (1) Arah orientasi serat berpengaruh terhadap kekuatan tarik dan bending komposit hibrid FML. Arah serat 00 mendapatkan hasil yang lebih besar daripada arah serat 900 yaitu dengan nilai kekuatan tarik rata-rata sebesar 98,7098925 Mpa dan kekuatan bending rata-rata sebesar 159,659941 Mpa. (2) Fraksi volume berpengaruh terhadap kekuatan tarik dan bending komposit hibrid FML. Fraksi volume 60% mendapatkan hasil yang lebih besar daripada fraksi volume 40% yaitu dengan nilai kekuatan tarik rata-rata sebesar 96,5237385 Mpa dan kekuatan bending rata-rata 148,808563 Mpa. (3) Paduan yang optimum antara arah serat dan fraksi volume yang memperoleh nilai kekuatan tarik dan bending terbesar yaitu pada arah serat 00 dan fraksi volume 60% dengan nilai kekuatan tarik rata-rata sebesar 115,2694 Mpa dan nilai kekuatan bending rata-rata sebesar 164.9409 Mpa.
Kata Kunci : Fibre Metal Laminate (FML), Komposut Hibrid, Uji Tarik, Uji bending

The development of sports from time to time continues to evolve in various aspects. In the past, sports only relied on muscle and mind strength. However, in an era where technology has become part of the necessities of life as it is now, sporting equipment has finally been developed to improve the performance of sports players. The increasing number of athletes will certainly have an impact on the intense competition. In tennis, one of the most seriously developed devices is a racket. To develop innovations in tennis racket material, it is necessary to innovate in the field of advanced materials, one of which is a hybrid composite laminated by the Fiber Metal Laminate (FML) method. The properties and mechanical strength of FML hybrid composites are influenced by several factors, one of which is the fiber direction and fiber volume fraction. To get the right combination of fiber direction and volume fraction, it is necessary to do a lot of research.
This research uses experimental research by making FML hybrid composite material with aluminum Al 6061 composite skin and laminate reinforced with hemp and e-glass fiber, each of which will be tested for bending and tensile tests. The specimens that have been tested for tensileand bending tests are then analyzed for the effect of the independent variables on the dependent variable. The independent variables include the fiber volume fraction of 40% and 60% of the fiber direction of 0o and 90o fibers.
Based on the results of the study, it can be concluded (1) The direction of fiber orientation affects the tensile strength and bending strength of the FML hybrid composite. The direction of the 00 fiber gets greater results than the direction of the 900 fiber, with an average tensile strength value of 98.70Mpa and an average bending strength of 159.65Mpa. (2) The volume fraction affects the tensile and bending strength of the FML hybrid composite. The volume fraction of 60% gets greater results than the volume fraction of 40%, with an average tensile strength value of 96.52MPa and an average bending strength of 148.80Mpa. (3) The optimum alloy between the direction of the fiber and the volume fraction that obtained the highest tensile strength and bending strength values is in the direction of the fiber 00 and the volume fraction of 60% with an average tensile strength value of 115.26MPa and an average bending strength value 164,94Mpa.
Keywords : Fibre Metal Laminate (FML), Hybrid Composite, Tensile test, bending test