Durabilitas Beton Geopolymer Berbasis Fly Ash Dengan NaOH 8 Molar Pada Daerah Agresif (Kondisi Laboratorium)
Durability Of Fly Ash Based Geopolymer Concrete With 8 Molar NaOH In Aggressive Areas (Laboratory Conditions)
Abu terbang (fly ash) merupakan bahan alternatif pengganti semen portland yang mampu memberikan dampak positif bagi lingkungan, dengan mengurangi gas emisi karbon dioksida yang dihasilkan dari produksi semen portland. Pemakaian abu terbang sendiri yaitu dengan mereaksi polimerisasi pada kandungan komponen alkali aktivator berupa sodium hidroksida 8 molar dan sodium silikat. Pada penelitian ini dilakukan perbandingan perilaku pada kondisi suhu ruang (normal) dan kondisi laboratorium dengan dua perilaku yakni direndam larutan asam pada pH 2,0-3,0 serta dimasukan simulasi tanah gambut pada pH 4,0-5,0 untuk mengetahui ketahanan beton geopolymer terhadap daerah agresif. Ketiga perilaku pada dua kondisi tiap benda uji dilakukan perawatan pada suhu ruang dan dioven dengan suhu 100°C selama 24 jam.
Pada penelitian ini menunjukan bahwa hasil kuat tekan rata-rata tertinggi dihasilkan oleh perilaku pada kondisi suhu ruang (normal). Pada usia 7 dan 28 hari kondisi suhu ruang (normal) mengalami peningkatan 17,6% dan 8,8%. Perilaku pada kondisi suhu ruang (normal) mengalami peningkatan sekitar 8,7% dari usia 28 hari sebesar 67,011 MPa. Sedangkan untuk kondisi laboratorium dengan dimasukan kedalam simulasi tanah gambut pada pH 4,0-5,0 usia 56 hari juga mengalami penurunan sekitar 1,5% dari usia 28 hari dengan kuat tekan sebesar 60,219 MPa. Dan untuk perilaku yang direndam larutan asam pada pH 2,0-3,0 usia 56 hari mengalami penurunan paling besar daripada kedua perilaku lainnya yakni sekitar 7,8% dari usia 28 hari dengan kuat tekan sebesar 56,345 MPa. Kuat tekan memiliki korelasi terhadap porositas, semakin tinggi nilai porositas pada beton geopolymer maka semakin rendah nilai kuat tekannya, begitu juga sebaliknya. Hasil uji porositas rata-rata terendah dihasilkan pada kondisi suhu ruang (normal), Pada usia 56 hari diperoleh 6,3%.
Kata kunci : Beton, abu terbang, porositas, kuat tekan, geopolymer, larutan asam, tanah gambut.
Fly ash is an alternative material to replace portland cement which is able to have a positive impact on the environment, by reducingcarbon dioxide emissions produced from the production of portland cement. The use of fly ash itself is by reacting polymerization to the content of alkaline activator components in the form of 8 molar sodium hydroxide and sodium silicate. In this study, a comparison was made between behavior at room temperature (normal) and laboratory conditions with two behaviors, namely soaking in an acid solution at pH 2.0-3.0 and inserting simulated peat soil at pH 4.0-5.0 to determine the resistance of concrete to Geopolymer for aggressive areas. The three behaviors in two conditions for each test object were treated at room temperature and baked in an oven at 100°C for 24 hours.
In this study it was shown that the highest average compressive strength results were produced by behavior at room temperature (normal) conditions. At the age of 7 and 28 days at room temperature (normal) there was an increase of 17.6% and 8.8%. Behavior at room temperature conditions (normal) increased by about 8.7% from 28 days of age of 67.011 MPa. As for the laboratory conditions, when it was put into the peat soil simulation at pH 4.0-5.0, the age of 56 days also decreased by around 1.5% from the age of 28 days with a compressive strength of 60.219 MPa. And for behavior soaked in acid solution at pH 2.0-3.0 aged 56 days experienced the greatest decrease than the other two behaviors, namely around 7.8% from 28 days of age with a compressive strength of 56.345 MPa. Compressive strength has a correlation with porosity, the higher the porosity value in concretegeopolymersthe lower the compressive strength value, and vice versa. The lowest average porosity test results were produced at room temperature conditions (normal). At the age of 56 days, 6.3% was obtained.
Keywords : Concrete, fly ash, porosity, compressive strength, geopolymer, acid solution, peat soil.