PENGARUH SUHU DAN WAKTU KALSINASI TERHADAP KEMURNIAN HIDROKSIAPATIT BERBASIS CANGKANG KERANG HIJAU UNTUK APLIKASI PADA BONE TISSUE ENGINEERING

THE EFFECT OF CALCINING TEMPERATURE AND TIME ON PURITY HYDROXYAPATITE BASED ON GREEN CELL SHELL FOR APPLICATION TO BONE TISSUE ENGINEERING

Hidroksiapatit merupakan material biokeramik berbasis kalsium fosfat dengan rumus kimia Ca₁₀(PO₄)₆(OH)₂ yang digunakan sebagai sel perancah. Hidroksiapatit sintetik yang umum digunakan masih harus di import dan memiliki harga yang mahal, Di Indonesia harga jual hidroksiapatit mencapai 1,5 Juta per 5 miligram. Komposit hidroksiapatit bisa didapatkan menggunakan sumber-sumber kalsium sintetik dan alami cangkang kerang hijau Untuk mendapatkan hidroksiapatit dapat dilakukan dengan metode, di antaranya metode pengendapan basah. Hidroksiapatit sintetis harus melalui proses kalsinasi, suhu dan waktu kalsinasi sangat berpengaruh terhadap kualitas hidroksiapatit sintesis. Pada penelitian ini hidroksiapatit dilakukan proses kalsinasi pada suhu 800°C Selama 4,5 jam, 5,5 jam, dan 6,5 jam dan sintesis hidroksiapatit dilakukan metode pengendapan basah atau presipitasi akan menghasilkan hidroksiapatit dengan tingkat kemurnian yang cukup tinggi. Hasil sintesis kemudian akan dilakukan karakterisasi menggunakan X-Ray Diffractometer (XRD) sehingga dapat diketahui fasanya dan Scanning Electron Microscope (SEM) untuk diuji penentuan morfologinya. HA Hasil dari uji XRD menunjukan hasil yang sama dengan hasil JCPDS no 09-0432 dimana dari ketiga sampel serbuk cangkang kerang hijau yang mempunyai intensitas kemurnian paling tinggi sampel variasi waktu 6,5 jam dengan sudut 2Theta 18,340, 29,630, 34,520. Sampel variasi 6,5 jam merupakan kondisi terbaik karena menghasilkan HA dengan kristalinitas 95,54%, parameter kisi, dan kemurnian 81,71% yang tinggi. Dari foto SEM memperlihatkan morfologi seperti granul dengan butir yang beragam, namun memiliki permukaan yang kasar. Dimana di variasi serbuk 6,5 jam lebih cenderung terjadi granul yang lebih banyak dibandingkan dengan sampel yang lain dikarenakan variasi waktu saat kalsinasi mempengaruhi kristalisasi dan bentuk morfologi. Kata Kunci: Hidroksiapatit, Kalsinasi, Cangkang Kerang Hijau, Metode Presipitasi. 

Hydroxyapatite is a calcium phosphate-based bioceramic material with the chemical formula Ca₁₀(PO₄)₆(OH)₂ used as a cell scaffold. The commonly used synthetic hydroxyapatite still has to be imported and has a high price. In Indonesia, the selling price of hydroxyapatite reaches 1.5 million per 5 milligrams. Hydroxyapatite composites can be obtained using synthetic and natural sources of calcium from green mussel shells. To obtain hydroxyapatite, several methods can be used, including the wet Precipitation Method. Synthetic hydroxyapatite must go through a calcination process, temperature and time of calcination greatly affect the quality of synthetic hydroxyapatite. In this study, the hydroxyapatite calcination process was carried out at 800°C for 4.5 hours, 5.5 hours, and 6.5 hours and the synthesis of hydroxyapatite was carried out using the wet deposition or precipitation method to produce hydroxyapatite with a fairly high level of purity. The results of the synthesis will then be characterized using an X-Ray Diffractometer (XRD) so that the phase can be identified and a Scanning Electron Microscope (SEM) to be tested for morphological determination. HA The results of the XRD test showed the same results as the results of JCPDS no 09-0432 where of the three samples of green mussel shell powder which had the highest intensity of purity the sample varied in time 6.5 hours with an angle of 2Theta 18.340 , 29.630 , 34.520. The 6.5 hours variation sample was the best condition because it produced HA with a high crystallinity of 95.54%, lattice parameters and 81.71% purity. The SEM photo shows a granular morphology with various grains, but has a rough surface. Where in the powder variation of 6.5 hours more granules tend to occur compared to other samples due to variations in calcination time affecting crystallization and morphological shape. Keywords: Hydroxyapatite, Calcination, Green Shells, Precipitation Method.