ANALYSIS OF CONCRETE COMPRESSIVE STRENGTH WITH ADDITIONAL CONSOL CR-93
Tulisan ini bertujuan untuk mengetahui kuat tekan beton silinder dengan rancang campur mutu fc’ 30 Mpa, dengan tambahan Consol CR-93 milik perusahaan Kimia Konstruksi Indonesia. Berdasarkan brosur Consol CR-93, bahan tambah ini bersifat polimer yang larut dalam air yang befungsi untuk meningkatkan kekuatan tekan beton dan mengurangi pemakaian semen dalam campuran.
Uji coba campuran beton dibagi dalam tiga perlakuan yaitu dengan dosis Consol CR-93 masing-masing 0,6%, 0,8%, dan 1% dari berat semen. Komposisi bahan campuran beton tersusun atas 20,40 kg semen, 53,5 kg agregat halus, 22,56 kg agregat kasar ukuran 5-12 mm, 41,82 kg agregat kasar ukuran 10-20 mm, air 7,6 kg.
Hasil uji kuat tekan pada beton silinder dengan bahan tambah Consol CR-93 sejumlah 0,6% pada umur 7 hari, 14 hari, dan 28 hari sebesar 22,16 MPa, 27,8 Mpa, dan 31,59 MPa. Kuat tekan beton silinder dengan bahan tambah Consol CR-93 sejumlah 0,8% pada umur 7 hari, 14 hari, dan 28 hari sebesar 25,27 MPa, 30,6 MPa, dan 34,77 MPa. Selanjutnya untuk kuat tekan beton silinder dengan bahan tambah Consol CR-93 sejumlah 1% pada umur 7hari, 14 hari, dan 28 hari sebesar 23,81 MPa, 29,2 MPa, dan 33,18 MPa.
This paper aims to determine the compressive strength of cylindrical concrete in a mixed design of 30 MPa, with the addition of Consol CR-93 from PT. Kimia Konstruksi Indonesia. According the the Consol CR-93 brochure, this admixture is a water-soluble polymer, which used to increase the compressive strength of concrete and reduce the use of cement in the mixture.
The concrete mix trial was divided into three treatments namely, with Consol CR-93 dosage of 0.6%, 0.8%, and 1% of the cement weight, respectively. The composition of the concrete mixture consists 20.40 kg of cement, 53.5 kg of fine aggregate, 22.56 kg of coarse aggregate with a size of 5-12 mm, 41.82 kg of coarse aggregate with a size of 10-20 mm, and 7.6 kg water.
The results showed that the compressive strength test on cylindrical concrete with 0.6% Consol CR-93 at the age of 7 days, 14 days, and 28 days were 22.16 MPa, 27.8 MPa, and 31.59 MPa. The compressive strength of cylindrical concrete with 0.8% Consol CR-93 at the age of 7 days, 14 days, and 28 days were 25.27 MPa, 30.6 MPa, and 34.77 MPa. The compressive strength of cylindrical concrete with 1% Consol CR-93 at the age of 7 days, 14 days, and 28 days were 23.81 MPa, 29.2 MPa, and 33.18 MPa.
Keywords: admixture, compressive strenght test, Consol CR-93