Efek Perlakuan Panas Artificial Aging Pada Al6061 Yang Dilapisi Nikel Chrome Terhadap Tingkat Kekerasan Dan Kekuatan Tarik

the effect of artificial aging heat treatment in al6061 chrome nickel coated on hardness and tensil strength level

       Penelitian ini dilakukan untuk meningkatkan nilai kekerasan dan kekuatan tarik dari material Al-6061 paduan yang akan digunakan sebagai bahan dasar pembuatan Propeller. Peningkatan kekerasan dan kekuatan material dilakukan dengan cara diberi perlakuan panas artificial aging dan dilapisi nikel-krom.

       Metode penelitian ini menggunakan penelitian jenis eksperimen. Material yang digunakan adalah paduan aluminium 6061, material dilakukan perlakuan panas artificial aging pada suhu 190°C dengan variasi waktu 1jam, 3jam, dan 5jam. Dan dilakukan elecroplating nikel-krom. Pengujian material menggunakan pengujian kekerasan rockwell Hardness Tester B dan pengujian tarik standar JIS Z2201.

          Berdasarkan data hasil penelitian, kekerasan material terendah adalah 113,9 HRB yang diperoleh dari material tanpa perlakuan artificial aging, sedangkan untuk nilai kekerasan tertinggi adalah 128,8 HRB diperoleh dari material dengan variasi waktu 5 jam artificial aging. Sedangkan nilai kekuatan tarik terendah adalah 23,7 MPa yang diperoleh dari material tanpa perlakuan artificial aging, sedangkan untuk nilai kekuatan tarik tertinggi adalah 27,4 MPa diperoleh dari material dengan variasi waktu 5 jam artificial aging. Dari pengujian kekerasan dan uji tarik pada material diketahui bahwa semakin lama waktu penahanan artificial aging maka semakin tinggi pula nilai kekerasan dan kekuatan tarik material yang diperoleh.

            This research was conducted to increase the hardness and tensile strength of the Al-6061 alloy material which will be used as the basic material for making propellers. Increasing the hardness and strength of the material is carried out by being treated with artificial aging and heat treatment nickel-chrome plated.

            This research method uses an experimental type of research. The material used is 6061 aluminum alloy, the material is heat treated by artificial aging at a temperature of 190°C with variations in time of 1 hour, 3 hours, and 5 hours. And nickel-chrome electroplating was carried out. Material testing uses Rockwell Hardness Tester B hardness test and JIS Z2201 standard tensile test.

                Based on research data, the lowest material hardness is 113.9 HRB obtained from material without artificial aging treatment, while the highest hardness value is 128.8 HRB obtained from material with a 5 hour artificial aging time variation. While the lowest tensile strength value is 23.7 MPa obtained from material without artificial aging treatment, while the highest tensile strength value is 27.4 MPa obtained from material with a 5 hour artificial aging time variation. From the hardness test and tensile test on the material, it is known that the longer the artificial aging holding time, the higher the hardness and tensile strength of the material obtained.