Analysis of Geopolymer Mortar Strength and Porosity Using Sidoarjo Mud as a Fly Ash Substitution Material with a 1: 5 Ratio Value Sand and 12 molar NaOH Activator in SS / SH 1.5 Conditions
Lumpur Sidoarjo adalah contoh lain bahan alam yang dimanfaatkan sebagai bahan subtitusi semen. Alasan penggunaan lumpur Sidoarjo karena jumlahnya melimpah dan dianggap mempunyai kandungan yang menyerupai semen, sehingga dapat digunakan sebagai bahan penyusun mortar geopolimer. Penelitian dilakukan untuk mengetahui pengaruh penggunaan lumpur Sidoarjo sebagai subtitusi fly ash yang ditinjau dari kuat tekan dan porositas mortar geopolimer. Perbandingan bahan pengikat dan pasir 1:5 dengan variasi penggunaan lumpur Sidoarjo sebesar 5%, 10%, 15%, 20%, 25%, 30%, 35%, 40%, 45%, 50%. Konsentrasi molaritas yang digunakan sebesar 12 Molar dengan perbandingan sodium silikat dan sodium hidroksida 1,5. Hasil penelitian menunjukan bahwa kadar optimum penggunaan lumpur Sidoarjo sebesar 5% dengan nilai kuat tekan 18,69 MPa dan porositas 13,78%. Peningkatan presentase lumpur Sidoarjo yang lebih besar menyebabkan penurunan kuat tekan dan peningkatan presentase porositas mortar geopolimer. Kata Kunci: geopolimer, lumpur Sidoarjo, fly ash, porositas, kuat tekan, mortar.
Sidoarjo mud is another example of natural materials which is used as a subtitute for cement. The reason for the use of Sidoarjo mud is that it is overflow and is considered to have a content similiar to cement, so it can be used as a constituent of geopolymer mortar. The study was conducted to determine the effect of the use of Sidoarjo mud as a substitution of fly ash in term of compressive strength and porosity of geopolymer mortars. Comparison of binder and sand 1:5 with variations in the use of Sidoarjo mud by 5%, 10%, 15%, 20%, 25%, 30%, 35%, 40%, 45%, 50%. The molarity concentration used was 12 Molar with a ratio of sodium silicate and sodium hydroxide 1,5. The results showed that the optimum level of using Sidoarjo mud was 5% with compressive strength of 18,69 MPa and porosity of 13,78%. Increasing the percentage of Sidoarjo mud is greater causing a decrease in compressive strength and an increase in the porosity of geopolymer mortar. Keywords: geopolymer, Sidoarjo mud, fly ash, porosity, compressive strength, mortar.