PENGARUH VARIASI ARUS DAN KECEPATAN ALIRAN GAS PELINDUNG PADA PENGELASAN MATERIAL SS-304 MENGGUNAKAN LAS TIG TERHADAP KEKUATAN TARIK DAN STRUKTUR MIKRO

THE EFFECT OF FLOW VARIATION AND PROTECTIVE GAS FLOW VARIATION ON SS-304 WELDING MATERIALS USING TIG WELDING ON PULLING STRENGTH AND MICRO STRUCTURE

Perkembangan teknologi dibidang kontruksi bertambah maju dalam bidang pengelasan karena memiliki pengaruh besar terhadap rekayasan. Berbagai peran penting dalam mempengaruhi hasil lasan supaya mendapat hasil lasan yang baik, salah satunya adalah kecepatan aliran gas pelindung dan arus lasan. Metode eksperimen digunakan dalam penelitian ini dengan memvariasikan kecepatan aliran gas pelindung dan arus lasan pada pengelasan TIG material baja tahan karat SS-304, yang nantinya masing-masing variabel dilakukan kekuatan tarik dan struktur mikro dengan tiga spesimen untuk masing-masing variabel. Spesimen yang sudah diuji tarik dan struktur mikro kemudian dianalisa berpengaruh dengan variabel bebas terhadap variabel terikat. Variabel bebas meliputi arus 80 A, 140 A dan kecepatan aliran gas pelindung 15 Liter/Menit dan 20 Liter/Menit. Berdasarkan penelitian ini dapat disimpulkan (1) Pada arus pengelasan dan kecepatan aliran gas pelindung berpengaruh pada kekuatan tarik baja tahan karat SS-304. Arus 140 A dan kecepatan aliran gas pelindung 20 Liter/Menit dengan kekuatan tarik rata-rata tertinggi sebesar 579,88 Mpa, sedangkan arus 80 A dan kecepatan aliran gas pelindung 15 Liter/Menit dengan kekuatan tarik rata-rata terkecil sebesar 500,74 Mpa. (2) Pada arus dan kecepatan aliran gas pelindung mengubah struktur mikro hasil pengelasan dengan bentuk fasa austenit terbesar didapat pada variasi arus 140 A dan kecepatan aliran gas pelindung 20 Liter/menit sedangkan bentuk fasa austenit terkecil didapat pada variasi arus 80 A dan kecepatan aliran gas pelindung 15 Liter/Menit.

Kata kunci: Las TIG, Arus Pengelasan,Gas Pelindung, SS-304, Kekuatan Tarik, Struktur Mikro.

Technological developments in the construction sector are advancing in the field of welding because they have a major influence on the foundation. There are various important roles in influencing the result of the weld in order to get a good weld result, one of which is the speed of the shielding gas flow and the flow of the weld. The experimental method is used in this research by varying the speed of the protective gas flow and the weld current in the TIG welding of SS-304 stainless steel material, where each variable is subjected to tensile strength and microstructure with three specimens for each variable. The specimens that have been tested for tensile and microstructure are then analyzed for their influence with the independent variable on the dependent variable. The independent variables include a flow of 80 A, 140 A and a protective gas flow rate of 15 Liter / Minute and 20 Liter / Minute. Based on this research, it can be concluded (1) The variation of the flow and flow rate of the protective gas has an effect on the tensile strength of stainless steel SS-304. The current is 140 A and the flow rate of the shielding gas is 20 Liter / Minute with the highest average tensile strength of 579.88 Mpa, while the current is 80 A and the flow rate of the shielding gas is 15 Liter / Minute with the smallest average tensile strength of 500.74 Mpa . (2) Variations in the flow and flow rate of the protective gas can change the microstructure of the welding results with the largest austenite phase form obtained at a current variation of 140 A and a flow rate of 20 liters of protective gas while the smallest austenite phase is obtained at a variation of current 80 A and flow velocity. protective gas 15 Liter / Minute.

Keywords: TIG Welding, Welding Current, Shielding Gas, SS-304, Tensile Strength, Micro Structure