Optimasi pH Kombinasi Ekstrak Bunga Telang (Clitoria ternatea) dan Daun Pisang Kering (Musa acuminate) sebagai Natural Dye Sensitizer pada Rangkaian DSSC (Dye Sensitized Solar Cell)

Optimation of pH Combination of Telang Flower (Clitoria ternatea) and Dry Banana Leaf (Musa acuminate) Extract as Natural Dye Sensitizer in DSSC (Dye Sensitized Solar Cell) Series

Penelitian ini mengenai pemanfaatan ekstrak Bunga Telang (Clitoria ternatea) dan Daun Pisang kering (Musa acuminate) sebagai natural dye sensitizer pada DSSC (Dye Sensitized Solar Cell). Kombinasi kedua ekstrak pewarna diharapkan mampu memperluas daerah serapan cahaya sehingga mampu meningkatkan kinerja rangkaian DSSC. Kombinasi ekstrak Bunga Telang dan Daun Pisang kering diperoleh melalui proses maserasi dengan perbandingan komposisi (b/b) antara Bunga Telang dan Daun Pisang kering adalah 1:1, 1:3, dan 3:1. Karakterisasi larutan pewarna dilakukan dengan analisis UV-Vis dan cyclic voltammetry dan diperoleh hasil terbaik pada larutan pewarna perbandingan 1:3 dengan energi bandgap 0,28462 eV. Komposisi pewarna terbaik diaplikasikan pada rangkaian DSSC dengan variasi pH 2, pH 7, dan pH 12 kemudian dilakukan pengukuran tegangan dan arus menggunakan multimeter sehingga diperoleh hasil V_OC 387 mV dan J­_SC 2,6 x 10^-3 mA.cm^-2 pada kondisi pH 2. Hasil penelitian ini menunjukkan perolehan efisiensi tertinggi terjadi pada pH 2 yaitu sebesar 2,88%.

This research is about the use of extracts of Telang Flower (Clitoria ternatea) and dry Banana Leaf (Musa acuminate) as natural dye sensitizer in DSSC (Dye Sensitized Solar Cell). The combination of the two dye extracts is expected to expand the light absorption area to improve the performance of the DSSC circuit. The combination of Telang Flower and dry Banana Leaf extract was obtained through the maceration process with the ratio (w/w) between Telang Flower and dry Banana Lead 1:1, 1:3, and 3:1. The characterization of the dye solution was carried out by UV-Vis analysis and cyclic voltammetry and the best results were obtained at 1:3 ratio of dye solution with a bandgap energy of 0,28462 eV. The best dye composition was applied to the DSSC series with variation of pH 2, 7, and 12 then measured the voltage and current using a multimeter to obtain the value of V_OC 387 mV and J_sc 2,6 x 10^-3 mA.cm^-2 at pH 2. The results showed that the highest efficiency gain occurred at pH 2 which is equal to 2,88%.