PENGARUH SUHU SINTERING TERHADAP KEMURNIAN HIDROKSIAPATIT BERDASAR TULANG SOTONG DENGAN METODE SOL-GEL
EFFECT OF SINTERING TEMPERATURE ON THE PURITY OF HYDROXYAPATITE BASED ON CUTTLEFISH BONES BY SOL-GEL METHOD
Hidroksiapatit adalah proses biokeramik material berbasis kalsium fosfat dengan rumus kimia Ca₁₀(PO₄)₆(OH)₂ yang digunakan sebagai sel scalfold. Untuk mendapatkan hidroksiapatit dapat dilakukan dengan beberapa metode, diantaranya metode sol-gel. Pada penelitian saat ini menggunakan metode sol-gel dan sumber kalsium yang dipakai adalah tulang sotong. Suhu dan waktu kalsinasi sangat memengaruhi kualitas hidroksiapatit sintesis. Pada penelitian ini hidroksiapatit dilakukan proses kalsinasi pada suhu 1000°C selama 3,5 jam lalu di lakukan sintering selama 6,5 jam dengan variasi suhu 550°C, 750°C, dan 950°C. Hasil dari sintetis tersebut akan dikarakterisasi menggunakan X-Ray Diffractometer (XRD) dan dapat diketahui fasanya sedangkan Scanning Electron Microscope (SEM) untuk diuji penentuan morfologinya. Diperoleh variasi suhu sintering pada proses sol-gel memiliki pengaruh pada kemurnian dan kristalinitas. Variasi suhu sintering pada proses sol-gel memiliki pengaruh terhadap tingkat kemurnian dan kristalinitas hidroksiapatit yang dihasilkan. Dari uji XRD sample dengan variasi suhu 950 memiliki tingkat kemurnian tertinggi 96,20% dengan tingkat kristalinitas sebesar 88,20%. bentuk morfologi yang di dapat, dalam penelitian ini hasil uji SEM menunjukkan bentuk morfologi granular yang beragam dan merapatnya antar partikel seiring meningkatnya variasi suhu, Bentuk terbaik dan juga kerapatan antar partikel terbaik terjadi pada sample dengan variasi suhu 950°C.
Kata Kunci : Hidroksiapatit, Kalsinasi, Metode Sol-Gel , Tulang Sotong.
Hydroxyapatite is a bioceramic process of calcium phosphate based materials with the chemical formula Ca₁₀(PO₄)₆(OH)₂ which is used as a scalfold cell. To get hydroxyapatite can be done by several methods, including the sol-gel method. In the current study, the sol-gel method is used and the source of calcium used is cuttlefish bone. The temperature and time of calcination greatly affect the quality of the synthetic hydroxyapatite. In this study, hydroxyapatite was calcined at a temperature of 1000°C for 3.5 hours and then sintered for 6.5 hours with temperature variations of 550°C, 750°C, and 950°C. The results of the synthesis will be characterized using an X-Ray Diffractometer (XRD) and the phase can be known while the Scanning Electron Microscope (SEM) will be tested to determine the morphology. It was obtained that the variation of sintering temperature in the sol-gel process had an effect on purity and crystallinity. The variation of the sintering temperature in the sol-gel process has an influence on the purity level and crystallinity of the hydroxyapatite produced. From the XRD test, the sample with a temperature variation of 950 has the highest purity level of 96.20% with a crystallinity level of 88.20%. morphological shape obtained, in this study the results of the SEM test showed a variety of granular morphological shapes and the closeness between the particles as the temperature variation increased, The best shape and also the best density between particles occurred in samples with temperature variations of 950°C.
Keywords : Hydroxyapatite, calcination, sol-gel method, cuttlefish.