PENGARUH TEGANGAN LISTRIK DAN WAKTU PENGELASAN TERHADAP KARAKTERISTIK FISIK DAN MEKANIK SAMBUNGAN LAS TITIK 3 LAPIS STAINLESS STEEL 304, 316, dan 317L
THE EFFECT OF ELECTRIC VOLTAGE AND WELDING TIME ON THE PHYSICAL AND MECHANICAL CHARACTERISTICS OF THE 3 LAYER WELDING EXPOSURE STAINLESS STEEL 304, 316, dan 317L
ABSTRAK
Nama : Muhammad Iqbal Pahlevi Noor
NIM : 15050754041
Program Studi : S1 Teknik Mesin
Jurusan/Fakultas : Teknik Mesin/Fakultas Teknik
Dosen Pembimbing : Dr. Yunus, M.Pd.
Perkembangan teknologi di zaman modern menuntut untuk semua pihak yang berkepentingan melakukan peningkatan kualitas dalam semua hal. Khususnya di bidang konstruksi yang sangat erat hubungannya dalam dunia produksi adalah proses pengelasan. Proses ini berpengaruh terhadap kualitas hasil lasan. Tujuan dari penelitian ini adalah untuk mengetahui tegangan geser material Stainless Steel 304, 316, 317L dengan perbedaan tegangan 2,30V, 2,67V, dan 3,20V serta waktu pengelasan 1s, 2s, dan 3s.
Metode yang digunakan pada penelitian ini adalah metode eksperimen, dengan melakukan eksperimen terhadap 27 spesimen uji yang dilas menggunakan las titik (Resistance Spot Welding). Penelitian dilakukan di Politeknik Negeri Malang. Pengujian untuk mengetahui tegangan geser hasil lasan adalah pengujian geser universal testing machine kemudian dilakukan uji anova dengan software IBM SPSS versi 23 untuk mengetahui perbandingan material.
Hasil penelitian menunjukkan pengaruh yang signifikan terhadap kekuatan geser pada pengelasan. Hal itu ditunjukkan dari hasil beban maksimum dan tegangan geser. Dalam hal ini pengaruh yang signifikan dijelaskan dalam dua perbedaan yakni perbedaan tegangan dan waktu, berikut adalah penjelasannya: (1) tegangan listrik sangat berpengaruh terhadap kekuatan geser pada pengelasan, hal itu ditunjukkan dari hasil beban maksimum dan tegangan geser yang didapatkan setiap kali tegangan listrik naik maka angka beban maksimum dan tegangan geser akan ikut naik; (2) Waktu pegelasan sangat berpengaruh terhadap kekuatan geser pada pengelasan, hal itu ditunjukkan dari hasil beban maksimum dan tegangan geser yang didapatkan setiap kali waktu penglesan naik maka angka beban maksimum dan tegangan geser akan ikut naik.
Kata kunci: Las titik (Resistance spot welding), Uji Tarik Geser Universal Testing Machine, Struktur Mikro
ABSTRACT
Name : Muhammad Iqbal Pahlevi Noor
Student ID Number : 15050754041
Study program : S1 of Mechanical Engineering
Department : Mechanical Engineering
Faculty : Technique
Institution : State University of Surabaya
Supervisor : Dr. Yunus, M.Pd.
Technological developments in modern times require all interested parties to improve quality in all aspects, especially in the construction field that is very closely related to the world production industry is welding. This process affects the quality of the welds. The purpose of this study was to determine the shear stress of stainless steel 304, 316, 317L with a difference in stress of 2.30V, 2.67V, and 3.20V and the welding time of 1s, 2s, and 3s.
The method used in this research is quantitative method and type of experimental research, by conducting experiments on 27 test specimens that are welded using point welding (Resistance Spot Welding). The research was conducted at the State Polytechnic of Malang. The test to determine the shear stress of the welds is a universal testing machine shear test, then anova test is carried out with the IBM SPSS version 23 software to determine the material comparison.
The results show a significant effect on the shear strength in welding. This is shown from the results of the maximum load and shear stress. In this case the significant effect is explained in two differences, in voltage and time, here is the explanation: (1) the electric voltage greatly affects the shear strength in welding, it is shown from the results of the maximum load and the shear stress obtained every time the electric voltage increases, then the maximum load and shear stress will increase. This is evidenced by the results of the t value obtained in the t test is below 0.05, so that a significant difference is obtained every time the voltage increases; (2) The time of welding greatly affects the shear strength of the welding, it is shown from the results of the maximum load and the shear stress obtained every time the application time increases, the maximum load and shear stress will increase. This is evidenced by the results of the t value obtained in the t test is below 0.05, so that a significant difference is obtained every time the voltage increases.
Keywords: Resistance spot welding, Universal Testing Machine, Micro Structure