PENGARUH ARTIFICIAL AGING PADA HASIL CORAN AL 6061 DENGAN METODE CENTRIFUGAL CASTING TERHADAP KEKUATAN TARIK DAN KEKERASAN
EFFECT OF ARTIFICIAL AGING ON TENSILE STRENGTH AND HARDNESS OF CASTING AL 6061 WITH CENTRIFUGAL CASTING METHOD
Alumunium 6061 adalah alumunium paduan yang sering digunakan untuk part-part otomotif maupun alat kontruksi. Alumunium 6061 memiliki unsur paduan Al 96,6%, Mg 1,15%, Mn 0,15%, Si 0,8%, Ti 0,15% dan Zn 0,25. Alumunium 6061 memiliki sifat-sifat yang memberi banyak keuntungan seperti tahan terhadap korosi, dapat diberi perlakuan panas, mempunyai ketangguhan yang baik, juga mampu las yang baik dan mampu cor yang baik. Karena mempunyai banyak sifat-sifat keuntungan inilah alumunium 6061 digunakan sebagai bahan utama otomotif, perancangan alat maupun kontruksi. Contoh pengaplikasikannya secara langsung seperti pada sepeda, velg, struktur rangka bangunan, struktur pesawat seperti sayap dan pesawat, gerbong kereta api, serta kontruksi kapal pesiar.
Jenis penelitian ini adalah penelitian eksperimen. Material yang digunakan dalam penelitian ini adalah aluminium 6061.Pengecoran dalam penelitian ini menggunakan metode centrifugal casting lalu diberikan perlakuan artificial aging dengan variasi temperature holding time. Variasi temperature holding time yang digunakan adalah 200⁰C, 250⁰C, dan 300⁰C selama 4 jam. Temperatur tuang yang digunakan adalah 740°C. Setelah melakukan pengecoran material dan artificial aging, lalu dilakukan uji tarik dan kekerasan.
Hasil dari penelitian pengaruh artificial aging dengan variasi temperatur holding time: tanpa artificial aging, 200⁰C, 250⁰C, dan 300⁰C menunjukkan nilai kekuatan tarik yang mengalami penurunan dan nilai kekerasan yang mengalami kenaikan. Nilai kekuatan tarik berturut-turut sebesar 163,49 MPa, 157,57 MPa, 146,46 MPa dan 137.15 MPa. Pada pengujian kekerasan berturu-turut mendapat nilai 82,70 HRB, 86,34 HRB, 87,32 HRB dan 95,68 HRB.
Aluminum 6061 is an aluminum alloy that is often used for automotive parts and construction tools. Aluminum 6061 has an alloying element of 96.6% Al, 1.15% Mg, 0.15% Mn, 0.8% Si, 0.15% Ti and 0.25 Zn. Aluminum 6061 has properties that provide many advantages such as corrosion resistance, can be heat treated, has good toughness, also has good weldability and good castability. Because it has many beneficial properties, aluminum 6061 is used as the main material for automotive, tool design and construction. Examples of its direct application include bicycles, wheels, building frame structures, aircraft structures such as wings and planes, train carriages, and cruise ship construction.
This type of research is experimental research. The material used in this study was aluminum 6061. Casting in this study used the cen-trifugal casting method and then subjected to artificial aging treatment with variations in temperature holding time. The temperature holding time variations used were 200⁰C, 250⁰C, and 300⁰C for 4 hours. The pouring temperature used is 740°C. After casting the material and artificial aging, tensile and hardness tests were carried out.
The results of the research on the effect of artificial aging with holding time temperature variations: without artificial aging, 200⁰C, 250⁰C, and 300⁰C show that the tensile strength value has decreased and the hardness value has increased. The tensile strength values are 163.49 MPa, 157.57 MPa, 146.46 MPa and 137.15 MPa respectively. In the successive hardness test, the scores were 82.70 HRB, 86.34 HRB, 87.32 HRB and 95.68 HRB.